POLIMAL VE-2MM is used for structurally durable part production. Vinylester resin is know for its high chemical resistance and they can be used to produce glassfibre, carbon laminates and polymerconcrete etc.
POLIMAL VE-2MM is best suited for use if high chemical resistance is needed. Parts created from this material preserve high strength properties in agressive enviroments. The resin is characterized by good production properties - good wettability with glassfibre and other cloths, after curing it leaves a solid surface.
Gel time 30 minutes.
After curing recommended in 60-80C for 3-6h.
Standard resin parameters
Viscosity,25 оС,
mPa, 300-350
Gel time, 25 ОС, min,
30±5
Flexural strength
mPa,
110
Tensile strength,
mPa,
75
Tensile modulus,
mPa,
3500
Heat deflection temp. HDT,
оС,
88
Barcol hardness,min
оВ,
28
Elongation at break % 2,5
Impact resistance,
kJ/ м2,
18
POLIMAL VE - 2MM 220 kg
VINYLESTER RESIN - POLIMAL VE - 2MM 220 kg
POLIMAL VE - 2MM 220 kg - FULL DRUMS | COMPOSITE24